Conclusion: Deformation and Resistance to Fatigue Loading

The aforementioned findings might have a crucial impact on our understanding of restoration reaction and resistance to cyclic forces. Specifically, the potential impact of the material's physical characteristics (ie, E-modulus and flexural strength) on medium- and long-term restoration behavior might largely depend on the extent of the preparation and the intrinsic capacity of the remaining tooth structure to resist functional stresses. In a vital tooth, it can be logically assumed that the restoration plays a less important protective role than it does in a nonvital configuration. In addition, a less rigid (significantly less than dentin; ie, nano-hybrid composite) or stiff and brittle material (ie, felspathic porcelain) would likely increase the risk of restoration/tooth failure when treating fragile teeth (nonvital) in high stress-bearing areas. The quality and consistency of the evidence here are satisfactory. However, the quantity of the evidence is rather limited, although such criteria seem less crucial as a result of the protocol applied (same tooth/teeth used for testing different cavity configurations or FEM stress simulation).

Only nondestructive tests or those involving cyclic loading were taken into consideration for this review because of the fact that mere resistance to fracture (“classical” fracture-resistance protocol) mimics the reaction of the system to extreme monotonic, linearly increasing stresses, and these are considered as poorly relevant as simulations for in vivo failures. Such tests neither reproduce accidental fracture (totally different stress kinetics) nor simulate other restoration failure patterns such as marginal leakage, tissue demineralization, pulpal complication, or fractures triggered by repeated stresses (fatigue). Likewise, the fracture patterns observed in such tests (which include axial or severe cusp and restoration fractures of vital tooth configurations) are practically nonexistent in vivo, with the exception of rather rare traumatic tooth fractures.⁵⁰ One can therefore assume that the quality of evidence would be insufficient, and this justifies the exclusion of such research in the present review.

Layering Techniques

When comparing different composite filling techniques (bulk, bulk + re-restoration and incremental) to amalgam restoration in Class II MOD cavities of different widths (1, 2.5, and 5 mm), more deformation resulted from adhesive techniques, with the highest deformation being measured in 5-mm bulk composite restorations.⁵¹ The concept of re-restoring a tooth involves the placement of a bulk-fill composite restoration that is fully polymerized, and then a new slot is subsequently cut into the composite after polymerization. This slot is subsequently restored with more composite, and this technique has been proposed as a means to dissipate stress in the final restored tooth. In this study, it was observed that re-restoration did reduce stress compared to initial values.

In Class I cavities, tooth deformation proved to be minimal in comparison to Class II MO (medium or large) or MOD cavities. The size and cavity design or configuration factor proved to be influential factors for tooth deformation⁵² and also for stress development. This occurred in an inverse relationship at the restorative interface, as measured directly on teeth and by FEM study.¹⁹ More recent studies have confirmed the increased deformation observed in Class II MOD restorations when compared to two-surface MO design⁵³ as well as the reduction of tooth deformation that is observed with layering techniques.⁵⁴ However, in this later study, no significant difference was observed between the horizontal and oblique layering techniques.

The deformation of intact and restored teeth using composite or ceramic in MOD cavities was also reviewed. The studies showed a mean tooth “compliance” of 2.0 (relative deformation) following preparation, and then the “compliance” reverted to 1.1 in the composite group and 1.0 in the ceramic group. This demonstrated the ability of both restorative materials to return the tooth's resistance to flexure under a load of 11.17 Kg.⁴²

Curing Protocols

Versluis and coworkers¹⁹ studied the effect of the curing protocol by using various combinations of light intensity and exposure time (but corresponding to similar curing energy) and observed large variations in shrinkage strain, as measured by both FEM and experimental methods. Their results actually revealed the positive impact of extending curing time with a reduced light intensity.¹⁹ Various curing light units and polymerization protocols where compared with regard to cuspal deflection of MOD restorations made of various materials (resin composites and an ormocer). The curing light type proved influential (LED induced less deformation), as did the restorative materials. The curing protocol of using a halogen curing unit (standard vs soft-start) had no influence on cuspal deformation³⁷; however, microleakage was observed to be inversely proportional to cuspal deformation, even though the authors could not explain the possible link between lower deformation and higher leakage.

Comparison of Materials and Brands

The influence of the composition of the matrix resin was also evaluated to assess cuspal flexure following the placement of each composite layer as well as after treatment completion. It was shown that the classical bisphenol A diglycidyl ether dimethacrylate and triethylene glycol dimethacrylate (TEGMA) resin blend augmented cuspal flexure compared to ethoxylated bisphenol A glycol dimethacrylate (Bis-EMA) and urethane dimethacrylate (UDMA ) compositions.⁵⁵ However, the authors did not comment on the material E-modulus, which largely differed among the tested materials and which is also likely to have influenced tooth deformation.

Electronic speckle pattern interferometry (ESPI) proved to be a viable method with which to monitor tooth dimensional changes during composite placement as the device doesn't contact the tooth.⁵⁶ The same authors also measured the influence of various composite systems on cuspal deflection following a single increment placement in 2 × 2.5 × 11-mm MOD cavities. The least amount of deformation was recorded with the experimental silorane system, while the flowable composite did not induce more deformation than a conventional hybrid. Among the nano-hybrid materials, variable, cumulative cusp displacement was also recorded, though it was significantly less than that associated with the conventional hybrid. The stiffness of the material proved once again to influence the reaction to composite polymerization shrinkage.

Fleming and coworkers^55,57 compared previous data obtained with a halogen light-curing unit (LCU) to new data generated with LED technology. Despite large numerical differences in favor of the ormocer material compared to the Z100 system, no statistical significance was revealed between both of these light-curing technologies.³⁷ The same authors investigated the cuspal deformation of experimental oxirane and silorane materials and compared it to that of monomodal composite systems (Z100 and Z250, 3M).⁴¹ They observed a significant reduction in cuspal deflection with the oxirane and then the silorane but with, respectively, an increase or no difference in microleakage values. The authors then put the relative “impact” of cuspal deformation on cavity seal into perspective.

Conclusion: Tooth Deformation and Shrinkage Stress

The cavity size and design (configuration factor) as well as material physico-chemical composition (filler and matrix and consequently the material's stiffness) proved to influence tooth deformation and stress development within the tooth structure or the restorative interface. When considering the design of the studies under review, the quality of the evidence has to be considered to be high, with good consistency. The light curing type (LED vs halogen) only proved to influence cuspal deformation (less deformation for LED curing) in some studies but had no influence on microleakage. The curing mode (soft-start vs conventional curing mode with halogen LCU) had no influence on either of these parameters. Therefore, the ability of a hypothetically “improved” curing approach, such as soft-start curing, appeared to be ineffective in reducing tooth deformation, while an extended curing time with continuous, lower irradiance did demonstrate reduced tooth deformation, even though it was tested in a different experimental setup. With regard to these hypotheses about curing modality, the quantity and consistency of the evidence were rather limited.

Conclusion: Tooth Deformation and Shrinkage Stress Methodology

The tooth deformation observed following the placement and polymerization of various composite materials and curing protocols validates the results obtained by FEM studies. Therefore, when measurements produced on natural teeth are compared to FEM, it confers on these tests a high quality of evidence. The ESPI approach without direct interference with the restored tooth appears to be a promising alternative to conventional strain gauges.

Comparison of Restorative and Layering Techniques

Several studies compared the influence of layering vs bulk-fill approaches on dentin bond-strength (BS). They all concluded that a bulk-fill technique did lead to lower bond strength compared to restorations placed incrementally.^58-61 The results regarding the influence of different layering approaches proved rather controversial, with some studies⁵⁹ showing higher bond strength values for the horizontal technique, while two other studies^58,60 concluded that there was no difference between horizontal and oblique or vertical layering techniques. When combining three to four horizontal and oblique layers in different geometries, the highest microtensile bond strength (MTBS) values were observed with the four increments. All other combinations of three horizontal and oblique layers exhibited similar MTBS values, and all were lower that that observed for four increments.⁶²

Other Restorative Variables (Cervical Margin Position, Cavity Dimensions, and C-Factor)

Cavity depth proved influential for bond strength, with lower values in deep dentin and the highest values observed on a flat preparation with low C-factor (CF=1). When a higher C-factor (CF=3) was used, all values fell, which demonstrated the impact of restricted free-surface and composite flow.⁶³ Consequently, the C-factor, and therefore bond strength, also proved to influence failure modes at the adhesive interface.⁶³ The cavity size was also shown to be an influential factor for dentin adhesion, and with an appropriate layering technique the negative impact of larger cavity dimensions could be counteracted.⁶¹ When attempts were made to evaluate the impact of preparation wall location (gingival, pulpal, and axial) on MTBS, no trend was found. The results actually demonstrated that adhesion was influenced by the adhesive system rather than by the preparation surface or location.⁶⁴

Sandwich Techniques

In one study,⁵⁸ the presence of a flowable resin composite (FRC) liner did not improve MTBS in Class II cavities restored incrementally using either a horizontal or oblique layering technique. In another study,⁶⁵ the differences in MTBS were specific to the product rather than influenced by the presence of a flowable composite liner underneath bulk or incrementally filled restorations. It was observed that a lining of FRC improved adhesion when vertical or oblique layering techniques were applied but had no apparent effect underneath horizontal increments. Once again, these findings were product specific.⁵⁹ Other authors concluded again that the use of a FRC liner alone did not improve MTBS underneath bulk-filled restorations with a high C-factor, while the presence of fibers or a combination or FRC together with fibers did increase MTBS.⁶⁶ Incorporation of glass fibers also showed stable BS values regardless of the C-factor.⁶⁶

Polymerization Protocol

Incremental techniques provided better MTBS than did bulk filling for the two different irradiation modes tested (continuous and stepped). MTBS values on flat dentin specimens were also higher than in a Class I cavity configuration, with the exception of the combination of incremental technique and stepped curing mode.⁶⁰ Different combinations of light sources (plasma, halogen and LED) were used to cure the dentin bonding agent (DBA) and composite in Class I cavities, and this revealed the significant influence of irradiation conditions. Overall, bond strength was more dependent on the light source used for curing the DBA rather than that used for curing the composite. In this study, the LED curing of the DBA together with halogen curing of the restorative composite produced the lowest MTBS values.⁶⁷

Comparison of Materials

Two adhesive systems (self-etch one and two step) were tested after mechanical and thermal fatigue. The one-step system presented lower MTBS values and more than 50% of sample debonding during the testing, which was presumably due to an overwet phenomenon. In this study,⁶⁸ the short period of mechanical loading (50,000 cycles) did not influence the results. In an attempt to evaluate the impact of contact time of the primer on the tooth substrate, additional priming times of 30, 60, and 120 seconds were added after normal application duration, but these did not influence MTBS, as measured on the gingival wall of Class II cavities.⁶⁹ In another study⁷⁰ from the same authors, it was concluded that MTBS values were not influenced by location (pulpal or gingival wall) for the various adhesives tested. However, the three-step total-etch, water-based adhesive and the two-step acetone-based prime and bond systems produced lower values than the two-step water-based self-etch and two-step total-etch ethanol-based systems.⁷⁰

Several composite types and brands were tested for polymerization shrinkage and their interface quality, microhardness profile, flexural strength, and elasticity-modulus following a bulk application in a Class I configuration. It was found that MTBS was correlated to elasticity modulus and the velocity of contraction stress development within restrictive cavity configuration.⁷¹ Therefore, one cannot predict that a high MTBS will be based only on a low E-modulus since the polymerization kinetics play an important role in the development of interfacial stresses and adhesion.⁷¹

Indirect Restorations

Various adhesives (one-step, two-step, and three-step systems) were compared following two modes (pre-cured or non–pre-cured) before the placement of indirect composite inlays. The effect of pre-curing appeared to be material and location specific, and the thickness of the adhesive layer appeared to be increased in the case of pre-curing.⁷² However, the relevance of the aforementioned results in relation to pre-curing the adhesive system for the cementation of indirect restorations would seem to be dubious since the concept of “dual bonding”⁷³ was not fully implemented in this study (adhesive layer thinned and light-cured just prior to adhesive cementation). This latter concept is also supported by more recent results^65,74 obtained on flat dentin or overlay-like preparations demonstrating that light-activation of the adhesive layer before indirect cementation, renamed “immediate dentin sealing,” is crucial to obtaining high MTBS.

The presence of temporary cement used for the interim restoration reduced MTBS values in Class I inlays, and to overcome this effect, cleaning of the cavity or immediate dentin sealing was needed.⁷⁵ The removal of cement excesses with a scaler or air polishing with a soft glass were effective treatments, while another air-polishing paste with round particles was unable to restore good MTBS values.⁷⁵

Comparison of Direct and Indirect Techniques

The effect of cyclic loading was evaluated on direct and indirect Class II composite restorations. It was shown⁷⁶ that next to marginal adaptation, MTBS values were superior in the indirect group. When evaluating the influence of different gererations of adhesives (third self-etch, fourth total etch, and fifth one bottle) in combination with direct composite and indirect ceramic restorations, the former multistep adhesive generations produced higher bond strengths, while the pre-curing of the adhesive before cementation of indirect restorations also increased the bond strength.⁷⁷ In a similar study configuration,⁷⁸ with simplified cavity design, the dual bonding concept once again noticeably increased the bond strength at buccal walls while reducing MTBS at pulpal walls. When interposing a layer of low-viscosity resin composite, the bond strength measurements were significantly lowered as a result of cohesive fractures in the low-filled liner. Interestingly, a comparison⁷⁹ between in vivo and in vitro MTBS bond strength on axial and gingival walls demonstrated lower values in vivo, which were particularly pronounced at the gingival walls, most likely as a result of higher substrate wetness.

Conclusion: Microtensile and Shear Tests

Within the limitations of this study protocol, the most relevant conclusions, based on a satisfactory quantity and consistency of the evidence, are that

• higher bond strengths were obtained with layering techniques (vs bulk);

• for indirect restorations, “dual bonding” or “immediate dentin sealing,” as opposed to an application and curing of the DBA just before placing the restoration, increased bond strength; and

• the cavity C-factor is an influential factor for bond strength (high CF reduces MTBS).

All other study variables, including curing protocols, cavity depth, the presence of flowable composite liner, light source, and various adhesive systems, did not have a clear impact on MTBS, and, therefore, no recommandationscan can be drawn as a result of the limited evidence related to quantity and consistency.

Conclusion: Microtensile and Shear Test Methodology

Bond strength and, in particular, microtensile bond strength tests measure the capacity of an adhesive interface to resist stresses induced by polymerization and occlusal function. They actually represent the first attempt to evaluate the potential of a specific restorative system or technique to establish the biomechanical balance needed to maintain sealed margins and reinforce the remaining tooth structure. Such features are crucial in Class I and II adhesive restorations in order to obtain satisfactory medium- and long-term clinical behavior. When combined with mechanical and thermal stressing (oral environment simulation), MTBS tests most likely increase their potential clinical relevance and adequately complement marginal adaptation studies. MTBS also have the potential to measure regional variations of bond strength, something that was not possible with conventional tensile or shear bond strength tests. However, this latter potential ability requires more investigation. The MTBS methodology does potentially suffer from tissue inhomogeneity, but on the other hand, it provides a precise, quantitative evaluation method, which confers an acceptable quality of evidence.

Comparison of Restorative and Layering Techniques

In the absence of mechanical loading, two studies^80,81 did not find any significant difference in marginal adaptation between bulk-fill and layering techniques, while a third report⁸² presented opposing findings of significantly more cervical defects in the bulk-fill technique group. In proximal microcavities, more sophisticated filling techniques, such as the three-site layering concept and ceramic inserts, did not show any advantage over a simple two-layer technique using either a restorative or flowable composite.⁸³ Accordingly, “overengineering” the restorative technique appeared useless for small volumes.

In an attempt to evaluate the benefit of additional retentions in small box preparations simulating restoration repair, the smallest box-only composite additions (without undercuts or occlusal retentions) provided the best resistance to cyclic loading.⁸⁴

Other Restorative Variables (Cervical Margin Position, Cavity Dimensions, Matrix Systems, etc)

The beveling of margins proved beneficial to marginal adaptation,^83,85,86 but mainly when enough tissue remained above the cemento-enamel junction.^87,88 When less than 1 mm of enamel height remained, the bevel no longer had a positive influence, and in such situations, an indirect technique provided better adaptation.⁸⁷ The instruments used for finishing and beveling margins proved to be influential with regard to marginal adaptation. Specifically, ultrasonic-driven instruments induced more marginal defects compared to sonic instruments^83,85 or a fine diamond round bur.⁸³ The vibration induced by ultrasonic energy during composite placement also proved to be beneficial for Class II adaptation of nonbeveled cavities.⁸⁵

Sandwich Techniques

Sandwich techniques with conventional glass ionomer cement as a lining downgraded the adaptation to dentin when compared to full composite restorations^87,88 or sandwich restorations using resin modified glass ionomer cement (rmGIC) liner or full composite restoration.⁸⁹ A rmGIC liner or base did show⁹⁰ the potential to improve marginal adaptation in vitro. The same potential was also demonstrated by a compomer; however, the adaption was only improved in a closed sandwich configuration.^86,91,92 But the rationale for using a fluoride-releasing material in an open sandwich configuration was finally questioned, as literature reviews^93,94 have not confirmed the protective role of GICs against recurrent caries. Other materials, such as chemically curing or flowable composites, were considered to facilitate restoration placement and/or reduce the negative impact of polymerization shrinkage. This literature review found that the presence of either a flowable liner or chemically curing composite base actually improved marginal adaption, but without totally suppressing marginal defects.^77,84,95,96 The aforementioned findings were confirmed recently another study,⁹⁷ which showed a significant reduction of imperfect margins after loading when applying rmGIC or flowable composite liners with lower E-modulus. In another study,⁹⁸ a positive effect was only observed when a thin, pre-cured flowable composite lining was applied. The cervical gap size in lined composite restorations was linearly correlated to the strain absorption capacity (negative correlation) and shrinkage (positive correlation).

Influence of Polymerization Protocol

It was first suggested by Goracci and de Martinis⁹⁹ that a slow polymerization mode could reduce marginal defects in Class II restorations. Since then, only a few reports have evaluated and confirmed the impact of curing protocol on the quality of adaptation in the Class II restoration. The adaptation to enamel of Class II MOD restorations was not influenced by the curing light energy (medium intensity conventional halogen or high-intensity plasma), while the step-curing protocol produced better occlusal and cervical adaption than did pulse-delay or ramp-curing protocols.¹⁰⁰ This partially supports other in vitro studies in which the authors studied the effect of various polymerization protocols on contraction force¹⁰¹ or distribution.¹⁹ In an attempt to confirm the advantage of the three-sided light-curing protocol over a conventional occlusal curing, it was shown that a reduced light intensity is likely to be the influential factor that improves restoration adaptation.¹⁰² In a recent study,¹⁰³ the impact of curing time and energy density on contraction stress and marginal adaptation was evaluated. It was shown that a minimal radiant exposure was needed to reach a satisfactory adaption and that a further increase in light density did not significantly affect contraction stress or adaptation. Nevertheless, relevant and conclusive studies clarifying the role and potential impact of curing protocols and light intensity on marginal adaptation are still needed.

Comparison Between Adhesive and Composite Types or Systems

Marginal adaptation to enamel was not affected by gingival fluid contamination when this happened just after acid etching. However, gingival fluid did adversely affect adaption when the contamination happened after adhesive placement.¹⁰⁴ These results should not necessarily be considered valid for blood or saliva contamination.

The use of a filled adhesive system improved the marginal and internal adaptation of mixed Class II cavities when compared to a nonfilled, thinner “prime and bond” adhesive system. The thicker and consequently elastic bonding resin was considered to act as a stress-breaking layer.⁹¹ The performance of simplified adhesive systems used with their respective composite also proved inferior to the multicomponent system that served as the control.¹⁰⁵

The comparison between ormocers and a traditional hybrid composite used in Class II cavities was clearly in favor of the hybrid composite, which presented very high percentages of perfect adaptation both in occlusal and cervical enamel. The adhesive used for the ormocer tested in this study was believed to be responsible for the unsatisfactory adaptation observed with the ormocer.¹⁰⁶ The influence of ceramic inserts on proximal adaptation of Class II restorations was dependant on the level of the cervical margin and the type of insert used.¹⁰⁷ Anatomically shaped inserts improved adaptation to enamel only, while round-shaped, beta-quartz inserts had no influence at all on adaptation when compared to full composite restorations. In dentin, the inserts had no positive impact on restoration quality.

Indirect Composite Restorations

The influence of resinous bases with increasing E-modulus underneath Class II MOD composite inlays was evaluated after mechanical loading. The best results were obtained with a “highly filled” flowable material, while the restorations having no base, a compomer, or a “low-filled” flowable or a restorative material lining showed more marginal defects.⁹² These results indicated that material mechanical properties such as rigidity/elasticity and viscosity have the potential to influence restoration adaptation after loading. It is interesting to mention that these differences appeared only after loading, which supports the use of cyclic loading to evaluate the impact of different materials or treatment protocols on Class II restoration adaptation and quality.

Comparison Between Direct and Indirect Class II Restorations

In the presence of thin cervical enamel (0.5-mm thickness and 1-mm height) the indirect composite restorations had a better adaptation compared to a direct, multilayered composite filling.⁸⁸ The presence of a bevel also improved the cervical adaptation in both direct and indirect restorations, but only when there was “thick” (>1 mm) enamel remaining. With a butt margin design, thick enamel was beneficial to indirect restorations only.⁸⁸ In a study⁸⁸ evaluating the influence of restorative technique (direct vs indirect composites) and liners (GIC or rmGIC), the inlay technique proved overall to be superior to the direct composite option. In this study, the presence of GIC or rmGIC liners lowered the excellent adaption percentages in both direct and indirect restorations. Once again, the benefit of glass ionomers used as liners was not substantiated by in vitro studies when evaluated in a protocol that was more clinically relevant.

The combination of the dual bonding technique (applying the adhesive system before impression or further restorative procedures)^73,108 together with an inlay or insert technique yielded better adaptation than did direct or indirect techniques using a conventional adhesive cementation technique (applying the adhesive at the time of cementation).¹⁰⁹ In addition, when comparing a direct technique to ceramic inlays using the dual bonding technique, better results were obtained with this latter approach.⁷⁷ Moreover, in this same study, third- and fourth-generation adhesives showed better performance than did those of the fifth generation. In another test,⁷⁶ in which the test samples underwent cyclic loading, the performance of composite inlays was observed to be superior to the direct technique. When comparing a direct technique to direct chair-side inlays or laboratory indirect inlays, the lowest amount of gaps was observed in the indirect group. A reduction in gaps was also observed in the direct inlay group compared to the group in which the direct technique was utilized, but this finding was not significant.¹¹⁰

Comparing different inlay materials in mixed Class II cavities (composite, low-fusing ceramic, Spinell and aluminous porcelains) did not show any significant difference in either marginal or cervical adaptation between these three ceramic materials, which had differing structure and stiffness.¹⁰⁹ The composite inlay, however, showed a better marginal adaptation in cervical dentin. In a similar study, the cement type appeared to be the influential factor for cervical adaptation to dentin. Better cervical adaptation to dentin was also observed with ceramic inlays compared to a direct technique, athough once again, this was dependant on the luting material.^1,110

Finally, it was observed that the proportion of gap-free resin-dentin interface was not influenced by the restorative technique (direct or CEREC inlay) but instead by the presence of a low-elasticity flowable composite liner, which significantly decreased the amount of defects at the same interface.¹¹¹

Evaluation of Marginal and Internal Adaptation of Class II Restorations Following Short-term Clinical Function

An interesting approach to testing the marginal and internal adaptation of Class II adhesive restorations was developed by van Dijken and coworkers.¹¹² They sought to integrate the clinical environment and strains, and their concept was to restore premolars scheduled to be extracted (one month after restoration placement) for orthodontic reasons and then to apply the same evaluation protocol as was used for in vitro investigations.¹¹² This approach confirmed the advantage of using a multicomponent adhesive system over a simplified one, and it also verified that the directed shrinkage technique (placing a base of self-curing composite underneath a light-curing restorative material) produced a dentin adaptation that was comparable to that obtained using a horizontal multilayering technique.¹¹² The adaptation for sandwich restorations using a compomer or rmGIC base was superior to full composite restorations after this short period of clinical service^113,114 and confirmed the findings of many in vitro investigations.^89-91 However, it has to be considered that these findings were not confirmed after longer in vivo observation periods.^115,116 Using the same protocol, the one-month adaption of Class II restorations with a FRC was observed to be equivalent to a full composite filling. Using this same test model and time frame, no influence on restoration adaptation was reported¹¹⁷ between a soft-start curing and continuous irradiation curing technique.

Conclusion: Marginal Adaptation

Within the limitations of this study protocol, the most relevant conclusions based on a satisfactory quantity and consistency of the evidence are that

• the position of restorative margins influenced the marginal adaptation (less defects observed at enamel margins);

• a bevel improved cervical adaptation in both direct and indirect restorations when enough enamel was present (>1 mm);

• the dual bonding technique (application of the adhesive system before impression and cementation) improved restoration adaptation;

• multicomponent adhesive systems showed better margins than did simplified ones;

• the use of a FRC with low E-modulus or a chemically curing composite base showed a potential for better marginal adaption underneath both direct and indirect restorations; and

• a better overall adaptation was obtained with indirect techniques.

The influence on marginal adaptation of other variables, such as the filling technique, the curing protocol and light intensity, the presence of a GIC or rmGIC liner, or the composite type used for direct restorations or material type (composites or ceramics) for indirect restorations, could not be ascertained as a result of the insufficient quantity or consistency of the available evidence.

Conclusion: Marginal Adaptation Methodology

Phenomena such as nano-leakage, leakage, pulpal complications, and secondary caries, which are induced by interface breakdown, represent the majority of clinical failures observed in all types of direct restorations.^3,118 Therefore, evaluating the behavior of adhesive restorations and interfaces with natural tissues under simulated function, pulpal pressure, and a moist environment helps to identify weak points and allows a better understanding of how to reduce the incidence of defects around or underneath a restoration.^92,119-121 This undoubtedly confers upon such a research approach the highest quality among all protocols used to test Class II restorations.

In fact, observing the restoration marginal adaptation without mechanical loading will only reflect the behavior of the system used to fabricate the restoration or placement/insertion stresses and will not provide information about the reaction of the overall system to function. Studies^{86,92,109,122} using multiple loading cycle steps have actually shown the impact of mechanical load magnitude and stress duration on the quality of marginal and internal adaptation of the restoration. For instance, a restorative system that exhibited a good immediate adaptation due to the increased flexibility of the liner later showed an unsuccessful behavior due to increased deformation under load and adverse behavior to fatigue once it was mechanically stressed. In other words, satisfactory initial adaptation of a restorative system can neither predict an optimal clinical behavior nor inform us about the reaction to long-term functional stresses or the oral cavity environment. The effect of long-term exposure to moisture is also an important test condition in order to reveal phenomena such as hydrolytic degradation and expansion of the restorative system due to water sorption.^115,116,123 The limited duration of in vitro investigations therefore still represents a weak aspect of such testing protocols and further justifies the need for in vivo trials, despite their numerous aforementioned practical limitations.

The sensitivity threshold and overall “quality” of evidence for marginal adaptation protocols should also be addressed, as procedural confounders exist for the laboratory stages (ie, control of sample moisture, polishing technique, experience of the operator, real load applied, etc), all of which can affect the significance of some studies and explain the conclusions of a recent and controversial review¹²⁴ questioning the relevance of marginal-internal adaptation tests of Class V restorations. As a result, the “apparent” absence of a correlation between clinical and in vitro studies regarding the performance of Class V restorations was erroneously interpreted as a possible irrelevance of marginal leakage tests instead of as an indication that confounders and sensitivity issues exist, which affect both the in vitro and clinical studies under review. This underlines once again the importance of extremely well-standardized study protocols and proper simulation of the oral environment (ie, functional loading) for in vitro trials.