Micro-shear Bond Strength of an Alternative Self-etch Application of “No Wait” Universal Adhesive to Caries-affected and Sound Dentin in Permanent and Primary Teeth
This study aimed to compare the micro-shear bond strength (μSBS) of caries-affected dentin (CAD) and sound dentin (SoD) in primary and permanent teeth using an alternative self-etch application of “no wait” universal adhesive. Flat midcoronal dentin surfaces from 72 permanent third molars and 72 second primary molars were distributed randomly into 12 groups according to the substrate SoD and artificially-created CAD (pH cycling for 14 days) and the adhesive system (GLUMA Bond5, a two-step etch & rinse adhesive, GLUMA Bond, a one-step self-etch adhesive, and Tokuyama Universal Bond, a one-step self-etch adhesive) (n=12). Bonded dentin resin discs were put through micro-shear bond strength testing after 10,000 thermocycles. The results were evaluated using two-way ANOVA and the Bonferroni test with a significance level of α = 0.05. When compared to SoD, the etch & rinse system's test results on artificially created CAD showed a statistically significant poorer bonding performance in both permanent and primary teeth in all groups (p<0.05). While the bond strengths of permanent teeth using total-etch adhesive on sound dentin were statistically significantly higher than those using Tokuyama Universal Bond adhesive (p<0.05), there was no significant difference in sound dentin in primary teeth (p>0.05). The etch & rinse system performed the poorest of all adhesive systems on CAD. The Tokuyama Universal Bond's adhesive strength was similar in SoD and CAD on primary teeth. The use of Tokuyama Universal Adhesives can speed up restorative treatment in pediatric dentistry.SUMMARY
Objective:
Methods and Materials:
Results:
Conclusions:
a): A universal testing machine and the arrows designate the location in the machine where the specimens are inserted. b): The specimens were placed in a universal testing machine.
Adhesive types’ micro-shear bond strength values (MPa).
Failure modes.